Jong-Kyu Baek
,
Hae-Wook Kwon
材料科学技术（英）
The effects of processing variables on the fluidity of hypereutectic Al-Si alloy melt during squeeze casting were investigated. The maximum fluidity of Al-16.0%Si alloy during squeeze casting was obtained under the applied pressure of 30 MPa. The fluidity increased with superheat. The fluidity increased with silicon content in the range from 12.0% to 20.0%. That was decreased respectively by eutectic modification and primary silicon refinement.
关键词:
Squeeze casting
,